C24 vs C50

C50 is 1.5 times as stiff as C24. It is 1.2 times as dense. Per unit mass C50 is 1.2 times as stiff. Strength: f_m,k = 24 MPa for C24, f_m,k = 50 MPa for C50.

C24 EN 338:2016 C50 EN 338:2016

Side by side

ratio = C50 / C24 · log scale

Property	C24	C50	Unit	Ratio
E₁ Modulus, direction 1	11	16	GPa	1.45×
E₂ Modulus, direction 2	0.37	0.53	GPa	1.43×
E₃ Modulus, direction 3	0.37	0.53	GPa	1.43×
G₁₂ Shear modulus 1-2	0.69	1	GPa	1.45×
G₁₃ Shear modulus 1-3	0.69	1	GPa	1.45×
E₀,₀₅ Modulus parallel to grain, 5 % fractile	7.4	10.7	GPa	1.45×
ρ Density	420	520	kg/m³	1.24×
ρ_k Density, characteristic (5 % fractile)	350	430	kg/m³	1.23×
f_m,k Bending strength	24	50	MPa	2.08×
f_t,0,k Tension parallel to grain	14.5	33.5	MPa	2.31×
f_t,90,k Tension perpendicular to grain	0.4	0.4	MPa	1×
f_c,0,k Compression parallel to grain	21	30	MPa	1.43×
f_c,90,k Compression perpendicular to grain	2.5	3	MPa	1.2×
f_v,k Shear strength	4	4	MPa	1×
E/ρ Specific stiffness E/ρ · derived	26.19	30.77	MJ/kg	1.17×
c₀ Bar wave speed √(E/ρ) · derived	5118	5547	m/s	1.08×
f/ρ Specific strength f/ρ · derived	57.14	96.15	kJ/kg	1.68×

Values at the first thickness band or product form of each material (EN 338:2016; EN 338:2016). A minimum and a characteristic value are not the same kind of number — read the ratio as a guide. Each material's page lists every band and every source.