C60/75 vs C80/95

C80/95 is 1.1 times as stiff as C60/75. Their densities are about the same. Per unit mass C80/95 is 1.1 times as stiff. Strength: f_ck = 60 MPa for C60/75, f_ck = 80 MPa for C80/95.

C60/75 EN 1992-1-1 C80/95 EN 1992-1-1

Side by side

ratio = C80/95 / C60/75 · log scale

Property	C60/75	C80/95	Unit	Ratio
E Young's modulus	39	42	GPa	1.08×
G Shear modulus	16.25	17.5	GPa	1.08×
ν Poisson's ratio	0.2	0.2	–	1×
ρ Density	2447	2447	kg/m³	1×
γ Weight density	24	24	kN/m³	1×
α Coefficient of thermal expansion	10	10	10⁻⁶/K	1×
f_ck Characteristic cylinder strength	60	80	MPa	1.33×
f_ck,cube Characteristic cube strength	75	95	MPa	1.27×
f_cm Mean cylinder strength	68	88	MPa	1.29×
f_ctm Mean tensile strength	4.4	4.8	MPa	1.09×
f_ctk,0.05 Tensile strength, 5 % fractile	3.1	3.4	MPa	1.1×
f_ctk,0.95 Tensile strength, 95 % fractile	5.7	6.3	MPa	1.11×
ε_c1 Strain at peak stress	2.6	2.8	‰	1.08×
ε_cu1 Ultimate strain	3	2.8	‰	0.933×
ε_c2 Strain at peak, parabola–rectangle	2.3	2.5	‰	1.09×
ε_cu2 Ultimate strain, parabola–rectangle	2.9	2.6	‰	0.897×
n Exponent, parabola–rectangle	1.6	1.4	–	0.875×
ε_c3 Strain at peak, bilinear	1.9	2.2	‰	1.16×
ε_cu3 Ultimate strain, bilinear	2.9	2.6	‰	0.897×
E/ρ Specific stiffness E/ρ · derived	15.94	17.16	MJ/kg	1.08×
c₀ Bar wave speed √(E/ρ) · derived	3992	4143	m/s	1.04×
f/ρ Specific strength f/ρ · derived	24.52	32.69	kJ/kg	1.33×

Values at the first thickness band or product form of each material (EN 1992-1-1; EN 1992-1-1). A minimum and a characteristic value are not the same kind of number — read the ratio as a guide. Each material's page lists every band and every source.