C50/60 vs C70/85

C70/85 is 1.1 times as stiff as C50/60. Their densities are about the same. Per unit mass C70/85 is 1.1 times as stiff. Strength: f_ck = 50 MPa for C50/60, f_ck = 70 MPa for C70/85.

C50/60 EN 1992-1-1 C70/85 EN 1992-1-1

Side by side

ratio = C70/85 / C50/60 · log scale

Property	C50/60	C70/85	Unit	Ratio
E Young's modulus	37	41	GPa	1.11×
G Shear modulus	15.42	17.08	GPa	1.11×
ν Poisson's ratio	0.2	0.2	–	1×
ρ Density	2447	2447	kg/m³	1×
γ Weight density	24	24	kN/m³	1×
α Coefficient of thermal expansion	10	10	10⁻⁶/K	1×
f_ck Characteristic cylinder strength	50	70	MPa	1.4×
f_ck,cube Characteristic cube strength	60	85	MPa	1.42×
f_cm Mean cylinder strength	58	78	MPa	1.34×
f_ctm Mean tensile strength	4.1	4.6	MPa	1.12×
f_ctk,0.05 Tensile strength, 5 % fractile	2.9	3.2	MPa	1.1×
f_ctk,0.95 Tensile strength, 95 % fractile	5.3	6	MPa	1.13×
ε_c1 Strain at peak stress	2.45	2.7	‰	1.1×
ε_cu1 Ultimate strain	3.5	2.8	‰	0.8×
ε_c2 Strain at peak, parabola–rectangle	2	2.4	‰	1.2×
ε_cu2 Ultimate strain, parabola–rectangle	3.5	2.7	‰	0.771×
n Exponent, parabola–rectangle	2	1.45	–	0.725×
ε_c3 Strain at peak, bilinear	1.75	2	‰	1.14×
ε_cu3 Ultimate strain, bilinear	3.5	2.7	‰	0.771×
E/ρ Specific stiffness E/ρ · derived	15.12	16.75	MJ/kg	1.11×
c₀ Bar wave speed √(E/ρ) · derived	3888	4093	m/s	1.05×
f/ρ Specific strength f/ρ · derived	20.43	28.6	kJ/kg	1.4×

Values at the first thickness band or product form of each material (EN 1992-1-1; EN 1992-1-1). A minimum and a characteristic value are not the same kind of number — read the ratio as a guide. Each material's page lists every band and every source.