C25/30 vs C30/37

C30/37 and C25/30 are about equally stiff. Their densities are about the same. Per unit mass they are about equally stiff (12.67 and 13.48 MJ/kg). Strength: f_ck = 25 MPa for C25/30, f_ck = 30 MPa for C30/37.

C25/30 EN 1992-1-1 C30/37 EN 1992-1-1

Side by side

ratio = C30/37 / C25/30 · log scale

Property	C25/30	C30/37	Unit	Ratio
E Young's modulus	31	33	GPa	1.06×
G Shear modulus	12.92	13.75	GPa	1.06×
ν Poisson's ratio	0.2	0.2	–	1×
ρ Density	2447	2447	kg/m³	1×
γ Weight density	24	24	kN/m³	1×
α Coefficient of thermal expansion	10	10	10⁻⁶/K	1×
f_ck Characteristic cylinder strength	25	30	MPa	1.2×
f_ck,cube Characteristic cube strength	30	37	MPa	1.23×
f_cm Mean cylinder strength	33	38	MPa	1.15×
f_ctm Mean tensile strength	2.6	2.9	MPa	1.12×
f_ctk,0.05 Tensile strength, 5 % fractile	1.8	2	MPa	1.11×
f_ctk,0.95 Tensile strength, 95 % fractile	3.3	3.8	MPa	1.15×
ε_c1 Strain at peak stress	2.1	2.2	‰	1.05×
ε_cu1 Ultimate strain	3.5	3.5	‰	1×
ε_c2 Strain at peak, parabola–rectangle	2	2	‰	1×
ε_cu2 Ultimate strain, parabola–rectangle	3.5	3.5	‰	1×
n Exponent, parabola–rectangle	2	2	–	1×
ε_c3 Strain at peak, bilinear	1.75	1.75	‰	1×
ε_cu3 Ultimate strain, bilinear	3.5	3.5	‰	1×
E/ρ Specific stiffness E/ρ · derived	12.67	13.48	MJ/kg	1.06×
c₀ Bar wave speed √(E/ρ) · derived	3559	3672	m/s	1.03×
f/ρ Specific strength f/ρ · derived	10.22	12.26	kJ/kg	1.2×

Values at the first thickness band or product form of each material (EN 1992-1-1; EN 1992-1-1). A minimum and a characteristic value are not the same kind of number — read the ratio as a guide. Each material's page lists every band and every source.